Template manufacturer wholesale

　　Hongshi Wood Industry Xiaohongban Series

　　Template layers: 7 layers, 8 layers, 9 layers, 10 layers, 11 layers, and 12 layers (10-12 layers need to be customized)

　　Specification: 1830X915X15mm ± 0.5mm Weight 15.5KG

　　Wood: Full grade wooden board with internal glue of cyanamide glue 80%+20% phenolic glue

　　Adhesive: 100% non melting phenolic resin hot pressing time 1050 seconds per board

　　Moisture content: 10% -12% Bonding strength 1.05 N/m ㎡

　　Tensile index: 39KG elastic modulus 10048 N/m ㎡

　　Nail insertion force: 28KG/nail insertion per time

　　Using imported first grade wood core material and two hot pressing molding processes to ensure a bright surface for each template and efficient turnover times.

　　Detailed introduction:

　　Building template specification: 1830 * 915 * (12-16) mm 1220 * 2440 (12-16) mm

　　Accepting customized building template prices from customers: factory direct sales, reasonable prices.

　　Product color: Red

　　Product thickness: 11mm-13mm 14mm, 14.5mm, 15mm, 16mm

　　Mold material: Waterproof paint (red)

　　Adhesive components: Phenolic Resin Adhesive (WBP), Triamine Adhesive.

　　Molding times: secondary molding of Hongshi building formwork.

　　1. Daily production of about 12000 sheets;

　　2. The process is a one-time molding process with one hot pressing and one cold pressing, adhering to the principle of unchanged process and superior quality;

　　3. The overall price is at a moderate level.

　　4. High rise building templates are made of high-quality full core boards as the main material, with no voids in the middle after sawing. The surface coating is a highly waterproof phenolic resin film, ensuring that each wooden template can achieve superior performance. It has the characteristics of no warping, no deformation, no cracking, high strength, and strong waterproofing.