Hongshi Wood Industry Black Building Coating Template Series

　　Template layers: 7 layers, 8 layers, 9 layers, 10 layers, 11 layers, and 12 layers (10-12 layers need to be customized)

　　Specification: 1830X915X15mm ± 0.5mm Weight 15.5KG

　　Wood: Full grade wooden board with internal glue of cyanamide glue 80%+20% phenolic glue

　　Adhesive: 100% non melting phenolic resin hot pressing time 1050 seconds per board

　　Moisture content: 10% -12% Bonding strength 1.05 N/m ㎡

　　Tensile index: 39KG elastic modulus 10048 N/m ㎡

　　Nail insertion force: 28KG/nail insertion per time

　　Using imported first grade wood core material and two hot pressing molding processes to ensure a bright surface for each template and efficient turnover times.

　　Detailed introduction:

　　Building template specification: 1830 * 915 * (12-16) mm

　　Accepting customized building template prices from customers: factory direct sales, reasonable prices.

　　Product color: Black

　　Product thickness: 11mm-13mm 14mm, 14.5mm, 15mm, 16mm

　　Mold surface material: laminated material (black)

　　Adhesive components: Phenolic Resin Adhesive (WBP), Triamine Adhesive.

　　Molding times: secondary molding of Hongshi building formwork.

　　1. Daily production of about 12000 sheets;

　　2. The process is a one-time molding process with one hot pressing and one cold pressing, adhering to the principle of unchanged process and superior quality;

　　3. The overall price is at a moderate level.

　　4. High rise building laminated boards are made of high-quality full core boards as the main material. After sawing, there are no holes in the middle of the board surface. The surface coating is made of highly waterproof laminated fabric, ensuring that each wooden template can achieve superior performance. It has the characteristics of no warping, no deformation, no cracking, high strength, and strong waterproofing.

　　5. The turnover times are 10-15 times or more, which is 3 to 5 times higher than ordinary templates, and the cost-effectiveness is extremely high.